Zheflon® FL2001 PVDF- Lithium battery Binders GradeDetail Information
Zheflon® FL2001 is a medium-viscosity polyvinylidene fluoride modified polymer that enhances the interaction between polymer molecules, active materials and metal plates, also improves the adhesion performance and corrosion resistance in the electrolyte, which especially suitable for Lithium cobaltate and lithium iron phosphate, that can effectively increase the bending resistance of pole pieces.
Zheflon® FL2001 can effectively reduce the amount of formula, reduce the DC resistance of the battery, improve the energy density and charge-discharge performance of the battery, effectively increase the capacity retention rate of the battery during the cycle, and thus meet the needs of the automotive industry.
Modified polymer, medium viscosity
Lithium battery binders
Water Absorption（%）(Time 24 hr)
Molecular weight distribution
Crystallization Temperature（DSC peak）（℃）
Glass Transition Temp, Tg（℃）
1% wt. loss / in air
Heat of Fusion（J/g）
After 2 min—500V
After 2 min@23℃
ASTM D2571.PVDF should be processed under 260℃,to avoid producing toxic gases；2.PVDF has good fire resistance and smoke inhibition property, however, when meets with fire, it will release toxic hydrogen fluoride gas and fluorocarbon compounds；3.Operators should take good care of personal protection during the use procedure and processing.
PVDF is packed in PE plastic bag and then be put into a drum with the net weight 25KGS. It must be stored in clean, cool, dry place.