Zheflon® FL2006 PVDF- Extrusion Grade
Categories PVDF Resin Album View larger image Brand Flurine Model FL2006 Features Homopolymer,Medium and low viscosity Uses Extruded pipe, Bar, Plate Forms Translucent white particles Processing technology Suspension PVDF Update Time 2021-01-23 Detail InformationZheflon®FL2006 PVDF homopolymer is medium and low viscosity grade that with high purity. Important properties include excellent chemical resistance to most aggressive substances and solvents, excellent mechanical strength and toughness, high abrasion resistance, high temperature capabilities, excellent aging resistance, low permeability to most gases and liquids and easily melt-processed by standard methods of extrusion.
General
Features
Homopolymer,Medium and low viscosity
Uses
Extruded pipe, Bar, Plate
Forms
Translucent white particles
Items
Typical Value FL2006
Test Method
Physical Properties
Density(g/cc)
1.77~1.79
ASTM D792
Melt Flow Rate(g/10min)
2.0~8.0
Load 5kg,230℃,ASTM D1238
Melt viscosity(Kps)
11~17
Shear Rate 100 1/s,ASTM D3835
Water Absorption(%)(Time 24 hr)
≤0.040
ISO 62
Linear Mold Shrinkage(cm/cm)
0.0200~0.0300
Molecular Properties
Molecular weight(Da)
300,000~390,000
GPC,DMF,ISO 16014
Intrinsic viscosity(dl/g)
1.00~1.20
30℃,DMAC
Molecular weight distribution
1.8-2.3
GPC,DMF,ISO 16014
Mechanical Properties
Tensile Modulus(Thickness2.00mm)(MPa)
1700~2500
1.0mm/min,ASTM D638
Flexural Modulus(Thickness2.00mm)(MPa)
1500~2300
2.0mm/min,ASTM D790
Yield Strength(Thickness2.00mm)(MPa)
50.0~57.0
50mm/min,ASTM D638
Break Strength(Thickness2.00mm)(MPa)
20.0~50.0
50mm/min,ASTM D638
Elongation at Yield(%)
5.0~10
50mm/min,ASTM D638
Elongation at Break(%)
20~50
50mm/min,ASTM D638
Hardness, Shore D(Thickness2.00mm)
75~80
ASTM D2240
Izod Impact, Notched(Thickness 4.00mm, 23℃)(J/m)
100~200
Notched V 10 mm
ASTM D256
Thermal Properties
Melting Point(℃)
169~173
ASTM D3418
Crystallization Temperature(DSC peak)(℃)
137~144
ASTM D3418
Glass Transition Temp, Tg(℃)
-32.0
ASTM E1356
Decomposition Temperature(℃)
375
1% wt. loss / in air
Vicat Softening Point(℃)
135~145
ASTM D1525
Heat deflection temperature at 1.8 MPa(Thickness 4.00mm)(℃)
102~110
After annealing 150℃,16h
ASTM D648
Electrical Properties
Surface Resistance(ohm)
≥1.00E+14
Voltage<1V,After 2 min—500V
ASTM D257
Electrical Resistivity(ohm·cm)
≥1.00E+14
Intensity=10mA,After 2 min@23℃
ASTM D257
Dielectric strength(Thickness 1.00mm,23℃)(KV/mm)
20~25
ASTM D149
Dielectric constant(1kHz,23℃)
7.0~10.0
ASTM D150
Burning Properties
UL Flame retardant grade(0.100mm)
V-0
UL94
Oxygen Index(3.00mm)
44%
ASTM D2683
1.PVDF should be processed under 260℃,to avoid producing toxic gases;2.PVDF has good fire resistance and smoke inhibition property, however, when meets with fire, it will release toxic hydrogen fluoride gas and fluorocarbon compounds;3.Operators should take good care of personal protection during the use procedure and processing.PVDF is packed in a plastic bag and then be put into a PE bag with the net weight 25KGS. It must be stored in clean, cool, dry place.
Please send your message to usCONTACT US TO GET DETAILED PRODUCT SPECIFICATIONS
- Contact us
Contact Person- leave a message:
- Contact Now
- Address:
- No.5, Weiyi Road, Shangyu Hangzhou Gulf Chemical Industrial Zone, Zhejiang, China 312369
subscriptionMobile pageCopyright © 2021 Zhejiang Fluorine Chemical New Materials Co., Ltd Support By BEE Cloud